Measurement of the absorption coefficient of a periodically poled LiNbO3 crystal at a radiation wavelength of 3 μm
- 1,2 Moscow Institute of Physics and Technology (MIPT) (Dolgoprudny, Russia)
- 3,4 Fryazino branch of Kotelnikov Institute of Radioengineering and Electronics of RAS (Fryazino, Russia)
Abstract
Problem formulating. In the case of nonlinear-optical conversion of high-power laser radiation in nonlinear-optical crystals the optical absorption leads to a nonuniform heating of the crystals, which results in the violation of phase matching conditions, the formation of defects, and optical damage.
Goal. Measurements of optical absorption coefficient of the periodically poled lithium niobate (PPLN) crystal at 3 μm radiation wavelength using the piezoelectric resonance laser calorimetry (PRLC).
Result. The optical absorption coefficient of PPLN crystal at 3.045 μm radiation wavelength was measured using the piezoelectric resonance laser calorimetry. The value (1.15±0.15) 10⋅ -2cm-1 of absorption coefficient within the measurement error limits was independent of the initial temperature of PPLN and the incident radiation power in the ranges 293–343 K and 0.2–10 W respectively.
Practical meaning. The interaction of mid-IR laser radiation with PPLN crystal was studied using the piezoelectric resonance laser calorimetry.
- Received
- 29.04.2021
- Approved after review
- 19.05.2021
- Accepted
- 27.05.2021
How to cite
Остапив А.Ю., Ларионов И.А., Коняшкин А.В., Рябушкин О.А. Определение коэффициента поглощения кристалла LiNbO3 с регулярной доменной структурой на длине волны излучения 3 мкм // Нелинейный мир. 2021. Т. 19. № 2. С. 39−42. DOI: https://doi.org/10.18127/j20700970-202102-09
References
- Ryabushkin O.A. et al. Equivalent temperature of nonlinear-optical crystals interacting with laser radiation. Journal of the European Optical Society-Rapid publications. 2011. V. 6. P. 11032.
- Pigarev A.V. et al. Impedance spectroscopy for measuring low optical absorption coefficients of nonlinear optical crystals. Proc. of SPIE. 2016. V. 9894. P. 98941T.