High-temperature low loss optical fibers
Keywords: optical loss microbending optical loss OH-groups
Authors:
S.M. Popov
Abstract:
The aim of the work is a researching additional optical loss of copper alloy coated optical fibers which were drawn from low hydroxyl group contamination preforms at temperatures up to 800 °C. It is reached that metal coated optical fiber worked at temperature 700 °C for 7 hours, while the optical losses changed from 2 to 3 dB/km at the wavelength of λ = 1300 nm.
Pages: 116-117
References
  1. Волошин В.В., Воробьев И.Л., Иванов Г.А., Исаев В.А., Колосовский А.О., Попов С.М., Чаморовский Ю.К. Влияние металлического покрытия на оптические потери при отжиге волоконных световодов // Письма в ЖТФ. 2009. Т. 35. № 8. С. 41-47.
  2. Волошин В.В., Воробьев И.Л., Иванов Г.А., Исаев В.А., Ленардич Б., Колосовский А.О., Попов С.М., Чаморовский Ю.К. Потери на поглощении света при высоких температурах в оптических волокнах с покрытием из алюминия или меди // Радиотехника и электроника. 2011. Т. 56. Вып.1. С. 103-110.
  3. Popov S.M., Voloshin V.V., Vorobyov I.L., Ivanov G.A., Kolosovskii A.O., Isaev V.A., Chamorovskii Y.K. Optical loss of metal coated optical fibers at temperatures up to 800 °С // Optical Memory and Neural Networks (Information Optics). 2012. V. 21. № 1. Р. 45-51.